Superpastic behavior was studied by mechanically working the cast material to varying degrees. The flow behavior was explored in the temperature range of 298 to 443 K and metallographic observations of longitudinal and transverse sections were made. Due to changes in microstructure and the nonunique stress-strain rate relation, the as-worked material is not suitable for assessing the mechanisms of superplastic flow based on steady state.