In this work, solution-processed low voltage organic field-effect transistors (OFETs) are demonstrated using P(VDF-TrFE) as the primary gate dielectric with TIPS-Pentacene: Polystyrene (PS) blend on top, providing an active layer. Maximum field-effect mobility of 0.6 cm2 V-1s-1 with an average of 0.4 (±0.1) cm2 V-1s-1 in saturation region and high Ion/Ioff value of 104 were achieved from these devices at an operating voltage of -5V. Moreover, these devices exhibited excellent electrical stability upon multiple scans of transfer characteristics and under bias-stress. A deterioration in the performance of OFETs was observed upon annealing at temperatures over 50 °C. © 2021 IEEE.